Lead (Pb) Pb1(ref)
 
Enthalpy Reference Temperature = Tr = 298.15 K Standard State Pressure = p° = 0.1 MPa
  J·K-1 mol-1 kJ·mol-1  
T/K Cp° S° -[G°-H°(Tr)]/T H-H°(Tr) fH° fG° log Kf
0 0. 0. INFINITE -6.878 0. 0. 0.
100 24.426 36.829 87.950 -5.112 0. 0. 0.
200 25.870 54.272 67.210 -2.587 0. 0. 0.
 
298.15 26.836 64.785 64.785 0. 0. 0. 0.
 
300 26.853 64.951 64.786 0.050 0. 0. 0.
400 27.723 72.796 65.849 2.779 0. 0. 0.
500 28.549 79.071 67.886 5.592 0. 0. 0.
 
600 29.404 84.336 70.201 8.481 0. 0. 0.
 
600.600 29.414 84.366 70.215 8.499 CRYSTAL <--> LIQUID
600.600 30.627 92.314 70.215 13.273 TRANSITION
 
700 30.332 96.984 73.693 16.303 0. 0. 0.
800 30.016 101.013 76.863 19.321 0. 0. 0.
900 29.698 104.530 79.746 22.306 0. 0. 0.
1000 29.397 107.643 82.383 25.261 0. 0. 0.
 
1100 29.091 110.431 84.808 28.185 0. 0. 0.
1200 28.786 112.949 87.050 31.079 0. 0. 0.
1300 28.652 115.247 89.132 33.950 0. 0. 0.
1400 28.623 117.368 91.074 36.812 0. 0. 0.
1500 28.673 119.344 92.893 39.677 0. 0. 0.
 
1600 28.786 121.198 94.605 42.549 0. 0. 0.
1700 28.928 122.948 96.221 45.435 0. 0. 0.
1800 29.109 124.606 97.753 48.336 0. 0. 0.
1900 29.296 126.185 99.208 51.256 0. 0. 0.
2000 29.497 127.693 100.595 54.196 0. 0. 0.
 
 
2019.022 29.541 127.972 100.851 54.758 LIQUID <--> IDEAL GAS
2019.022 24.831 215.927 100.851 232.340 FUGACITY = 1 bar
 
2100 25.499 216.916 105.308 234.378 0. 0. 0.
2200 26.365 218.122 110.408 236.971 0. 0. 0.
2300 27.261 219.314 115.118 239.652 0. 0. 0.
2400 28.173 220.493 119.484 242.423 0. 0. 0.
2500 29.084 221.662 123.547 245.286 0. 0. 0.
 
2600 29.979 222.820 127.343 248.240 0. 0. 0.
2700 30.844 223.968 130.901 251.281 0. 0. 0.
2800 31.669 225.105 134.245 254.407 0. 0. 0.
2900 32.444 226.230 137.398 257.613 0. 0. 0.
3000 33.160 227.342 140.377 260.894 0. 0. 0.
 
3100 33.813 228.440 143.200 264.243 0. 0. 0.
3200 34.398 229.523 145.881 267.654 0. 0. 0.
3300 34.913 230.589 148.432 271.120 0. 0. 0.
3400 35.360 231.639 150.864 274.635 0. 0. 0.
3500 35.737 232.669 153.186 278.190 0. 0. 0.
 
3600 36.048 233.680 155.408 281.780 0. 0. 0.
3700 36.296 234.672 157.537 285.398 0. 0. 0.
3800 36.485 235.642 159.580 289.037 0. 0. 0.
3900 36.618 236.592 161.542 292.693 0. 0. 0.
4000 36.700 237.520 163.430 296.359 0. 0. 0.
 
4100 36.737 238.427 165.248 300.031 0. 0. 0.
4200 36.733 239.312 167.001 303.705 0. 0. 0.
4300 36.692 240.176 168.693 307.377 0. 0. 0.
4400 36.619 241.019 170.327 311.042 0. 0. 0.
4500 36.518 241.841 171.907 314.699 0. 0. 0.
 
4600 36.395 242.642 173.436 318.345 0. 0. 0.
4700 36.252 243.423 174.917 321.978 0. 0. 0.
4800 36.093 244.185 176.352 325.595 0. 0. 0.
4900 35.923 244.927 177.744 329.196 0. 0. 0.
5000 35.743 245.651 179.095 332.779 0. 0. 0.
 
5100 35.557 246.357 180.407 336.344 0. 0. 0.
5200 35.367 247.046 181.682 339.890 0. 0. 0.
5300 35.175 247.717 182.922 343.417 0. 0. 0.
5400 34.985 248.373 184.128 346.925 0. 0. 0.
5500 34.796 249.013 185.302 350.414 0. 0. 0.
 
5600 34.612 249.639 186.445 353.885 0. 0. 0.
5700 34.434 250.250 187.559 357.337 0. 0. 0.
5800 34.263 250.847 188.645 360.772 0. 0. 0.
5900 34.097 251.431 189.704 364.189 0. 0. 0.
6000 33.942 252.003 190.738 367.590 0. 0. 0.
 
PREVIOUS: March 1962 (1 atm) CURRENT: March 1962 (1 bar)
 
Lead (Pb) Pb1(ref)

Download table in tab-delimited text format.