Lead (Pb)								Pb1(cr,l)
Enthalpy Reference Temperature = Tr = 298.15 K								Standard State Pressure = p° = 0.1 MPa
		J·K-1 mol-1						kJ·mol-1
T/K		Cp°		S°		-[G°-H°(Tr)]/T		H-H°(Tr)		fH°		fG°		log Kf
0		0.		0.		INFINITE		-6.878		0.		0.		0.
100		24.426		36.829		87.950		-5.112		0.		0.		0.
200		25.870		54.272		67.210		-2.587		0.		0.		0.
250		26.363		60.096		65.225		-1.282		0.		0.		0.
298.15		26.836		64.785		64.785		0.		0.		0.		0.
300		26.853		64.951		64.786		0.050		0.		0.		0.
400		27.723		72.796		65.849		2.779		0.		0.		0.
500		28.549		79.071		67.886		5.592		0.		0.		0.
600		29.404		84.336		70.201		8.481		0.		0.		0.
600.600		29.414		84.366		70.215		8.499		CRYSTAL <--> LIQUID
600.600		30.627		92.314		70.215		13.273		TRANSITION
700		30.332		96.984		73.693		16.303		0.		0.		0.
800		30.016		101.013		76.863		19.321		0.		0.		0.
900		29.698		104.530		79.746		22.306		0.		0.		0.
1000		29.397		107.643		82.383		25.261		0.		0.		0.
1100		29.091		110.431		84.808		28.185		0.		0.		0.
1200		28.786		112.949		87.050		31.079		0.		0.		0.
1300		28.652		115.247		89.132		33.950		0.		0.		0.
1400		28.623		117.368		91.074		36.812		0.		0.		0.
1500		28.673		119.344		92.893		39.677		0.		0.		0.
1600		28.786		121.198		94.605		42.549		0.		0.		0.
1700		28.928		122.948		96.221		45.435		0.		0.		0.
1800		29.109		124.606		97.753		48.336		0.		0.		0.
1900		29.296		126.185		99.208		51.256		0.		0.		0.
2000		29.497		127.693		100.595		54.196		0.		0.		0.
2019.022		29.541		127.972		100.851		54.758		FUGACITY = 1 bar
2100		29.706		129.137		101.920		57.156		177.221 7.115 0.177
2200		29.920		130.524		103.189		60.138		-176.833		15.884		-0.377
2300		30.133		131.859		104.406		63.140		-176.511		24.636		-0.560
2400		30.347		133.146		105.577		66.164		-176.259		33.376		-0.726
2500		30.556		134.389		106.705		69.210		-176.077		42.107		-0.880
2600		30.761		135.591		107.793		72.275		-175.964		50.832		-1.021
2700		30.962		136.756		108.844		75.362		-175.920		59.553		-1.152
2800		31.171		137.885		109.861		78.468		-175.939		68.275		-1.274
2900		31.376		138.983		110.847		81.595		-176.018		76.998		-1.387
3000		31.581		140.050		111.802		84.743		-176.151		85.725		-1.493
PREVIOUS:								CURRENT: March 1962
Lead (Pb)								Pb1(cr,l)

Download table in tab-delimited text format.