Silicon (Si)								Si1(l)
Enthalpy Reference Temperature = Tr = 298.15 K								Standard State Pressure = p° = 0.1 MPa
		J·K-1 mol-1						kJ·mol-1
T/K		Cp°		S°		-[G°-H°(Tr)]/T		H-H°(Tr)		fH°		fG°		log Kf
0
100
200
250
298.15		27.196		44.460		44.460		0.		48.470		40.826		-7.152
300		27.196		44.628		44.461		0.050		48.483		40.778		-7.100
350		27.196		48.821		44.792		1.410		48.808		39.467		-5.890
400		27.196		52.452		45.527		2.770		49.082		38.114		-4.977
450		27.196		55.655		46.478		4.130		49.317		36.728		-4.263
500		27.196		58.521		47.542		5.490		49.523		35.318		-3.690
600		27.196		63.479		49.797		8.209		49.867		32.443		-2.824
700		27.196		67.671		52.059		10.929		50.139		29.517		-2.203
800		27.196		71.303		54.243		13.648		50.349		26.556		-1.734
900		27.196		74.506		56.320		16.368		50.507		23.572		-1.368
1000		27.196		77.372		58.284		19.088		50.616		20.573		-1.075
1100		27.196		79.964		60.139		21.807		50.679		17.565		-0.834
1200		27.196		82.330		61.891		24.527		50.700		14.554		-0.634
1300		27.196		84.507		63.548		27.246		50.679		11.542		-0.464
1400		27.196		86.522		65.118		29.966		50.616		8.534		-0.318
1500		27.196		88.399		66.608		32.686		50.512		5.531		-0.193
1600		27.196		90.154		68.026		35.405		50.365		2.537		-0.083
1685.000		27.196		91.562		69.178		37.717		CRYSTAL <--> LIQUID
1700		27.196		91.803		69.376		38.125		0. 0. 0.
1800		27.196		93.357		70.666		40.844		0.		0.		0.
1900		27.196		94.827		71.899		43.564		0.		0.		0.
2000		27.196		96.222		73.081		46.284		0.		0.		0.
2100		27.196		97.549		74.215		49.003		0.		0.		0.
2200		27.196		98.814		75.304		51.723		0.		0.		0.
2300		27.196		100.023		76.353		54.442		0.		0.		0.
2400		27.196		101.181		77.363		57.162		0.		0.		0.
2500		27.196		102.291		78.338		59.882		0.		0.		0.
2600		27.196		103.358		79.280		62.601		0.		0.		0.
2700		27.196		104.384		80.191		65.321		0.		0.		0.
2800		27.196		105.373		81.073		68.040		0.		0.		0.
2900		27.196		106.327		81.928		70.760		0.		0.		0.
3000		27.196		107.249		82.756		73.480		0.		0.		0.
3100		27.196		108.141		83.561		76.199		0.		0.		0.
3200		27.196		109.005		84.343		78.919		0.		0.		0.
3300		27.196		109.842		85.103		81.638		0.		0.		0.
3400		27.196		110.653		85.842		84.358		0.		0.		0.
3500		27.196		111.442		86.562		87.078		0.		0.		0.
3504.616		27.196		111.478		86.595		87.203		FUGACITY = 1 bar
3600		27.196		112.208		87.264		89.797		384.152 10.461 0.152
3700		27.196		112.953		87.949		92.517		-383.738		21.417		-0.302
3800		27.196		113.678		88.616		95.236		-383.326		32.361		-0.445
3900		27.196		114.385		89.268		97.956		-382.915		43.295		-0.580
4000		27.196		115.073		89.904		100.676		-382.505		54.218		-0.708
4100		27.196		115.745		90.526		103.395		-382.096		65.131		-0.830
4200		27.196		116.400		91.135		106.115		-381.687		76.034		-0.946
4300		27.196		117.040		91.730		108.834		-381.279		86.927		-1.056
4400		27.196		117.665		92.312		111.554		-380.871		97.811		-1.161
4500		27.196		118.277		92.882		114.274		-380.462		108.686		-1.262
PREVIOUS: December 1966								CURRENT: March 1967
Silicon (Si)								Si1(l)

Download table in tab-delimited text format.