Silicon (Si)								Si1(cr,l)
Enthalpy Reference Temperature = Tr = 298.15 K								Standard State Pressure = p° = 0.1 MPa
		J·K-1 mol-1						kJ·mol-1
T/K		Cp°		S°		-[G°-H°(Tr)]/T		H-H°(Tr)		fH°		fG°		log Kf
0		0.		0.		INFINITE		-3.218		0.		0.		0.
100		7.268		3.833		33.351		-2.952		0.		0.		0.
200		15.636		11.665		20.531		-1.773		0.		0.		0.
250		18.221		15.446		19.138		-0.923		0.		0.		0.
298.15		20.000		18.820		18.820		0.		0.		0.		0.
300		20.050		18.943		18.820		0.037		0.		0.		0.
350		21.276		22.132		19.069		1.072		0.		0.		0.
400		22.142		25.032		19.636		2.159		0.		0.		0.
450		22.803		27.680		20.385		3.283		0.		0.		0.
500		23.330		30.110		21.237		4.436		0.		0.		0.
600		24.154		34.440		23.086		6.812		0.		0.		0.
700		24.803		38.212		24.983		9.260		0.		0.		0.
800		25.359		41.562		26.850		11.769		0.		0.		0.
900		25.874		44.579		28.655		14.331		0.		0.		0.
1000		26.338		47.329		30.387		16.942		0.		0.		0.
1100		26.778		49.860		32.044		19.598		0.		0.		0.
1200		27.196		52.208		33.627		22.297		0.		0.		0.
1300		27.614		54.401		35.142		25.037		0.		0.		0.
1400		28.033		56.463		36.592		27.820		0.		0.		0.
1500		28.451		58.411		37.982		30.644		0.		0.		0.
1600		28.870		60.261		39.317		33.510		0.		0.		0.
1685.000		29.225		61.765		40.412		35.979		CRYSTAL <--> LIQUID
1685.000		27.196		91.562		40.412		86.187		TRANSITION
1700		27.196		91.803		40.864		86.595		0.		0.		0.
1800		27.196		93.357		43.738		89.315		0.		0.		0.
1900		27.196		94.827		46.388		92.034		0.		0.		0.
2000		27.196		96.222		48.846		94.754		0.		0.		0.
2100		27.196		97.549		51.133		97.473		0.		0.		0.
2200		27.196		98.815		53.272		100.193		0.		0.		0.
2300		27.196		100.023		55.279		102.913		0.		0.		0.
2400		27.196		101.181		57.167		105.632		0.		0.		0.
2500		27.196		102.291		58.950		108.352		0.		0.		0.
2600		27.196		103.358		60.638		111.071		0.		0.		0.
2700		27.196		104.384		62.239		113.791		0.		0.		0.
2800		27.196		105.373		63.762		116.511		0.		0.		0.
2900		27.196		106.327		65.214		119.230		0.		0.		0.
3000		27.196		107.249		66.600		121.950		0.		0.		0.
3100		27.196		108.141		67.925		124.669		0.		0.		0.
3200		27.196		109.005		69.196		127.389		0.		0.		0.
3300		27.196		109.842		70.415		130.109		0.		0.		0.
3400		27.196		110.653		71.586		132.828		0.		0.		0.
3500		27.196		111.442		72.714		135.548		0.		0.		0.
3504.616		27.196		111.478		72.765		135.673		FUGACITY = 1 bar
3600		27.196		112.208		73.800		138.267		384.152 10.461 0.152
3700		27.196		112.953		74.848		140.987		-383.738		21.417		-0.302
3800		27.196		113.678		75.861		143.707		-383.326		32.361		-0.445
3900		27.196		114.385		76.840		146.426		-382.915		43.295		-0.580
4000		27.196		115.073		77.787		149.146		-382.505		54.218		-0.708
4100		27.196		115.745		78.704		151.865		-382.096		65.131		-0.830
4200		27.196		116.400		79.594		154.585		-381.687		76.034		-0.946
4300		27.196		117.040		80.458		157.305		-381.279		86.927		-1.056
4400		27.196		117.665		81.296		160.024		-380.871		97.811		-1.161
4500		27.196		118.277		82.111		162.744		-380.462		108.686		-1.262
PREVIOUS:								CURRENT: March 1967
Silicon (Si)								Si1(cr,l)

Download table in tab-delimited text format.