Titanium (Ti) Ti1(l)
 
Enthalpy Reference Temperature = Tr = 298.15 K Standard State Pressure = p° = 0.1 MPa
  J·K-1 mol-1 kJ·mol-1  
T/K Cp° S° -[G°-H°(Tr)]/T H-H°(Tr) fH° fG° log Kf
0              
100              
200              
250              
 
298.15 27.638 39.181 39.181 0. 13.652 11.141 -1.952
 
300 27.639 39.352 39.181 0.051 13.657 11.126 -1.937
350 27.667 43.614 39.518 1.434 13.752 10.696 -1.596
400 27.694 47.310 40.266 2.818 13.810 10.255 -1.339
450 27.722 50.574 41.234 4.203 13.838 9.809 -1.139
500 27.750 53.496 42.316 5.590 13.842 9.360 -0.978
 
600 27.805 58.560 44.614 8.368 13.794 8.468 -0.737
700 27.860 62.851 46.921 11.151 13.689 7.587 -0.566
800 27.916 66.573 49.150 13.939 13.552 6.725 -0.439
900 28.104 69.871 51.272 16.739 13.361 5.882 -0.341
1000 28.423 72.847 53.283 19.564 13.065 5.066 -0.265
 
1100 28.875 75.576 55.188 22.428 12.614 4.286 -0.204
1200 29.459 78.113 56.993 25.343 8.035 3.674 -0.160
1300 30.175 80.498 58.711 28.324 8.035 3.311 -0.133
1400 31.023 82.765 60.348 31.383 8.035 2.948 -0.110
 
1460.000 31.595 84.078 61.297 33.261 GLASS <--> LIQUID
1460.000 47.237 84.078 61.297 33.261 TRANSITION
 
1500 47.237 85.355 61.921 35.150 8.652 2.576 -0.090
 
1600 47.237 88.404 63.482 39.874 10.121 2.122 -0.069
1700 47.237 91.267 65.033 44.598 11.473 1.580 -0.049
1800 47.237 93.967 66.566 49.321 12.693 0.962 -0.028
1900 47.237 96.521 68.076 54.045 13.768 0.281 -0.008
 
1939.000 47.237 97.481 68.658 55.887 BETA <--> LIQUID
 
2000 47.237 98.944 69.560 58.769 0. 0. 0.
 
2100 47.237 101.249 71.014 63.493 0. 0. 0.
2200 47.237 103.446 72.439 68.216 0. 0. 0.
2300 47.237 105.546 73.833 72.940 0. 0. 0.
2400 47.237 107.557 75.197 77.664 0. 0. 0.
2500 47.237 109.485 76.530 82.388 0. 0. 0.
 
2600 47.237 111.338 77.833 87.111 0. 0. 0.
2700 47.237 113.120 79.107 91.835 0. 0. 0.
2800 47.237 114.838 80.353 96.559 0. 0. 0.
2900 47.237 116.496 81.571 101.283 0. 0. 0.
3000 47.237 118.097 82.762 106.006 0. 0. 0.
 
3100 47.237 119.646 83.927 110.730 0. 0. 0.
3200 47.237 121.146 85.067 115.454 0. 0. 0.
3300 47.237 122.600 86.182 120.178 0. 0. 0.
3400 47.237 124.010 87.274 124.901 0. 0. 0.
3500 47.237 125.379 88.343 129.625 0. 0. 0.
 
3600 47.237 126.710 89.391 134.349 0. 0. 0.
 
3630.956 47.237 127.114 89.711 135.811 FUGACITY = 1 bar
 
3700 47.237 128.004 90.417 139.072 409.098 7.788 0.110
3800 47.237 129.264 91.423 143.796 -407.864 19.039 -0.262
3900 47.237 130.491 92.409 148.520 -406.685 30.258 -0.405
4000 47.237 131.687 93.376 153.244 -405.560 41.447 -0.541
 
4100 47.237 132.853 94.324 157.967 -404.488 52.609 -0.670
4200 47.237 133.991 95.255 162.691 -403.467 63.745 -0.793
4300 47.237 135.103 96.169 167.415 -402.495 74.858 -0.909
4400 47.237 136.189 97.066 172.139 -401.570 85.948 -1.020
4500 47.237 137.250 97.948 176.862 -400.691 97.018 -1.126
 
PREVIOUS: September 1966 CURRENT: June 1979
 
Titanium (Ti) Ti1(l)

Download table in tab-delimited text format.