		J·K^-1 mol^-1						kJ·mol^-1
Titanium (Ti)								Ti₁(cr,l)

Enthalpy Reference Temperature = T_r = 298.15 K								Standard State Pressure = p° = 0.1 MPa
T/K		C_p^°		S^°		-[G^°-H^°(T_r)]/T		H-H^°(T_r)		_fH^°		_fG^°		log K_f
0		0.		0.		INFINITE		-4.830		0.		0.		0.
100		14.334		8.261		50.955		-4.269		0.		0.		0.
200		22.367		21.227		32.989		-2.352		0.		0.		0.
250		24.074		26.414		31.169		-1.189		0.		0.		0.

298.15		25.238		30.759		30.759		0.		0.		0.		0.

300		25.276		30.915		30.760		0.047		0.		0.		0.
350		26.169		34.882		31.071		1.334		0.		0.		0.
400		26.862		38.423		31.772		2.660		0.		0.		0.
450		27.418		41.620		32.692		4.018		0.		0.		0.
500		27.877		44.534		33.733		5.401		0.		0.		0.

600		28.596		49.683		35.973		8.226		0.		0.		0.
700		29.135		54.134		38.257		11.114		0.		0.		0.
800		29.472		58.039		40.490		14.039		0.		0.		0.
900		30.454		61.561		42.639		17.030		0.		0.		0.
1000		32.074		64.848		44.697		20.151		0.		0.		0.

1100		34.334		68.006		46.673		23.466		0.		0.		0.

1166.000		36.175		70.058		47.938		25.791		ALPHA <--> BETA
1166.000		29.245		73.636		47.938		29.963		TRANSITION

1200		29.459		74.479		48.679		30.961		0.		0.		0.
1300		30.175		76.864		50.756		33.941		0.		0.		0.
1400		31.023		79.131		52.702		37.000		0.		0.		0.
1500		32.003		81.304		54.537		40.150		0.		0.		0.

1600		33.115		83.404		56.276		43.405		0.		0.		0.
1700		34.359		85.448		57.932		46.778		0.		0.		0.
1800		35.736		87.451		59.517		50.281		0.		0.		0.
1900		37.244		89.422		61.039		53.929		0.		0.		0.

1939.000		37.868		90.186		61.617		55.394		BETA <--> LIQUID
1939.000		47.237		97.481		61.617		69.540		TRANSITION

2000		47.237		98.944		62.734		72.421		0.		0.		0.

2100		47.237		101.249		64.513		77.145		0.		0.		0.
2200		47.237		103.446		66.233		81.869		0.		0.		0.
2300		47.237		105.546		67.897		86.592		0.		0.		0.
2400		47.237		107.557		69.508		91.316		0.		0.		0.
2500		47.237		109.485		71.069		96.040		0.		0.		0.

2600		47.237		111.338		72.582		100.764		0.		0.		0.
2700		47.237		113.120		74.051		105.487		0.		0.		0.
2800		47.237		114.838		75.477		110.211		0.		0.		0.
2900		47.237		116.496		76.863		114.935		0.		0.		0.
3000		47.237		118.097		78.211		119.659		0.		0.		0.

3100		47.237		119.646		79.523		124.382		0.		0.		0.
3200		47.237		121.146		80.800		129.106		0.		0.		0.
3300		47.237		122.600		82.045		133.830		0.		0.		0.
3400		47.237		124.010		83.259		138.554		0.		0.		0.
3500		47.237		125.379		84.443		143.277		0.		0.		0.

3600		47.237		126.710		85.598		148.001		0.		0.		0.

3630.956		47.237		127.114		85.951		149.463		FUGACITY = 1 bar

3700		47.237		128.004		86.727		152.725		409.098 7.788 0.110
3800		47.237		129.264		87.830		157.449		-407.864		19.039		-0.262
3900		47.237		130.491		88.908		162.172		-406.685		30.258		-0.405
4000		47.237		131.687		89.963		166.896		-405.560		41.447		-0.541

4100		47.237		132.853		90.995		171.620		-404.488		52.609		-0.670
4200		47.237		133.991		92.005		176.343		-403.467		63.745		-0.793
4300		47.237		135.103		92.994		181.067		-402.495		74.857		-0.909
4400		47.237		136.189		93.964		185.791		-401.570		85.948		-1.020
4500		47.237		137.250		94.914		190.515		-400.691		97.018		-1.126

PREVIOUS:								CURRENT: June 1979

Titanium (Ti)								Ti₁(cr,l)

Download table in tab-delimited text format.