Tungsten (W) W1(l)
 
Enthalpy Reference Temperature = Tr = 298.15 K Standard State Pressure = p° = 0.1 MPa
  J·K-1 mol-1 kJ·mol-1  
T/K Cp° S° -[G°-H°(Tr)]/T H-H°(Tr) fH° fG° log Kf
0              
100              
200              
250              
 
298.15 24.296 45.678 45.678 0. 46.896 43.015 -7.536
 
300 24.310 45.828 45.678 0.045 46.896 42.991 -7.485
350 24.642 49.601 45.975 1.269 46.896 42.340 -6.319
400 24.928 52.911 46.640 2.508 46.896 41.689 -5.444
450 25.144 55.859 47.503 3.760 46.896 41.038 -4.764
500 25.359 58.519 48.474 5.023 46.896 40.388 -4.219
 
600 25.790 63.181 50.547 7.580 46.896 39.086 -3.403
700 26.229 67.190 52.645 10.181 46.896 37.784 -2.819
800 26.669 70.721 54.688 12.826 46.896 36.482 -2.382
900 27.112 73.887 56.648 15.515 46.896 35.180 -2.042
1000 27.564 76.767 58.518 18.249 46.896 33.879 -1.770
 
1100 28.017 79.416 60.299 21.028 46.896 32.577 -1.547
1200 28.472 81.873 61.996 23.852 46.896 31.275 -1.361
1300 28.930 84.170 63.614 26.722 46.896 29.973 -1.204
1400 29.393 86.331 65.160 29.638 46.896 28.672 -1.070
1500 29.862 88.375 66.640 32.601 46.896 27.370 -0.953
 
1600 30.334 90.317 68.060 35.611 46.896 26.068 -0.851
1700 30.806 92.170 69.424 38.668 46.896 24.766 -0.761
1800 31.284 93.944 70.737 41.772 46.896 23.465 -0.681
1900 31.768 95.649 72.004 44.925 46.896 22.163 -0.609
2000 32.254 97.291 73.228 48.126 46.897 20.861 -0.545
 
2100 32.745 98.876 74.411 51.376 46.897 19.559 -0.487
2200 33.238 100.411 75.558 54.675 46.897 18.258 -0.433
2300 33.735 101.899 76.672 58.024 46.897 16.956 -0.385
2400 34.233 103.345 77.753 61.422 46.897 15.654 -0.341
 
2450.000 34.483 104.054 78.283 63.140 GLASS <--> LIQ
2450.000 35.564 104.054 78.283 63.140 TRANSITION
 
2500 35.564 104.772 78.805 64.918 46.944 14.352 -0.300
 
2600 35.564 106.167 79.831 68.475 47.005 13.047 -0.262
2700 35.564 107.509 80.831 72.031 46.992 11.740 -0.227
2800 35.564 108.803 81.807 75.587 46.870 10.437 -0.195
2900 35.564 110.051 82.760 79.144 46.600 9.140 -0.165
3000 35.564 111.256 83.690 82.700 46.155 7.855 -0.137
 
3100 35.564 112.423 84.598 86.257 45.491 6.589 -0.111
3200 35.564 113.552 85.485 89.813 44.577 5.348 -0.087
3300 35.564 114.646 86.352 93.369 43.388 4.139 -0.066
3400 35.564 115.708 87.200 96.926 41.889 2.972 -0.046
3500 35.564 116.739 88.030 100.482 40.015 1.853 -0.028
 
3600 35.564 117.741 88.841 104.039 37.665 0.795 -0.012
 
3680.000 35.564 118.522 89.478 106.884 CRYSTAL <--> LIQUID
 
3700 35.564 118.715 89.635 107.595 0. 0. 0.
3800 35.564 119.663 90.413 111.151 0. 0. 0.
3900 35.564 120.587 91.175 114.708 0. 0. 0.
4000 35.564 121.488 91.922 118.264 0. 0. 0.
 
4100 35.564 122.366 92.653 121.821 0. 0. 0.
4200 35.564 123.223 93.371 125.377 0. 0. 0.
4300 35.564 124.060 94.075 128.933 0. 0. 0.
4400 35.564 124.877 94.766 132.490 0. 0. 0.
4500 35.564 125.676 95.444 136.046 0. 0. 0.
 
4600 35.564 126.458 96.110 139.603 0. 0. 0.
4700 35.564 127.223 96.764 143.159 0. 0. 0.
4800 35.564 127.972 97.406 146.715 0. 0. 0.
4900 35.564 128.705 98.037 150.272 0. 0. 0.
5000 35.564 129.423 98.658 153.828 0. 0. 0.
 
5200 35.564 130.818 99.868 160.941 0. 0. 0.
5400 35.564 132.161 101.039 168.054 0. 0. 0.
5600 35.564 133.454 102.174 175.167 0. 0. 0.
5800 35.564 134.702 103.274 182.279 0. 0. 0.
6000 35.564 135.908 104.342 189.392 0. 0. 0.
 