Zirconium, Alpha (Zr)	Zr1(cr)
T(K)	Cp	S	-[G-H(Tr)]/T	H-H(Tr)	delta-f H	delta-f G	log Kf
0	0.	0.	INFINITE	-5.497	0.	0.	0.
100	18.617	14.055	60.166	-4.611	0.	0.	0.
200	23.873	29.050	41.140	-2.418	0.	0.	0.
250	24.693	34.474	39.281	-1.202	0.	0.	0.
298.15	25.202	38.869	38.869	0.	0.	0.	0.
300	25.218	39.025	38.870	0.047	0.	0.	0.
350	25.606	42.943	39.178	1.318	0.	0.	0.
400	25.935	46.384	39.868	2.606	0.	0.	0.
450	26.246	49.457	40.766	3.911	0.	0.	0.
500	26.564	52.238	41.776	5.231	0.	0.	0.
600	27.281	57.143	43.939	7.922	0.	0.	0.
700	28.053	61.406	46.136	10.689	0.	0.	0.
800	28.966	65.210	48.287	13.538	0.	0.	0.
900	30.003	68.680	50.363	16.486	0.	0.	0.
1000	31.128	71.899	52.357	19.542	0.	0.	0.
1100	32.306	74.921	54.272	22.713	0.	0.	0.
1135.000	32.724	75.939	54.925	23.851	ALPHA <--> BETA
1200	33.502	77.783	56.113	26.004	3.711 0.222  0.010
1300	34.681	80.511	57.886	29.413	-3.170	0.528	-0.021
1400	35.807	83.123	59.596	32.938	-2.556	0.790	-0.029
1500	36.846	85.630	61.249	36.572	-1.886	1.006	-0.035
1600	37.762	88.038	62.848	40.304	-1.181	1.176	-0.038
1700	38.520	90.351	64.398	44.119	-0.466	1.301	-0.040